| Customization: | Available |
|---|---|
| Type: | Conveyor Belt |
| Feature: | Wear-resistant, Heat-resistant, Tear-resistant, Flame-resistant, Cold-resistant |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Heat Resistant Ep Fabric Conveyor Belt
Product Desription
Heat resistant conveyor belt is mainly used to transport high temperature materials, such as sintering ore, hot coke, clinker, hot casting and so on. According to the manifestation of the heat resistant belt breakage until to lose transportation ability and the heat resistant grading, we use EDPM or SBR as the covering layer rubber, and high modulus low shrinkage polyester or cotton canvas as the strong layer. It can use the heat resistant woven glass fabric between the cover rubber and the layers, so as to improve the working life of the heat resistant conveyor belt. We can make it into endless conveyor belt as per cllients' requirement.
|
The physical and mechanical properties of the heat resistant covering layer after tested should be in accordance with the following table: |
|||||
| Project | The type | ||||
| T1 | T2 | T3 | T4 | ||
| Change the range | |||||
| Hardness | Draw the intensity | 20 | 20 | 20 | 20 |
| Maximum after wearing out | 85 | ||||
| Draw the intensity |
The minimum value Mpa after wearing out |
12 | 10 | 5 | 5 |
| Performance rate of change /% | -25 | -30 | -40 | -40 | |
| Break person who extend | Performance rate of change /% | -50 | -50 | -55 | -55 |
| After aging rate of change /% | 200 | 200 | 180 | 180 | |
The heat resistance conveyor belt physical property of the cover rubber after heat test shall conform to the values specified in the table.
| Item | type | ||||||
| type I | type II | type III | |||||
| variable range | |||||||
| Hardness | Difference before and after ageing (IRHD) | ±20 | |||||
| Max. Value after ageing (IRHD) | 85 | ||||||
| Tensile strength | variable rate in performance <= | 25 | 30 | 40 | |||
| Min. value after ageing Mpa | 12 | 10 | 5 | ||||
| Rate of elongation at break | variable rate in performance% <= | 50 | 55 | ||||
| Min. value after ageing | 200 | 180 | |||||
The heat resistance conveyor belt abrasive wear of the cover rubber
| Type Item level | Abrasive wear | ||
| type I | type II | type III | |
| First quality | 0.8 | 1 | 1 |
| accepts | 1 | 1.2 | 1.2 |
The heat resistance conveyor belt layer to layer adhesion strength
| Item |
interlayer of cloth |
cover layer and cloth interlayer | |
|
Thickness of the cover layer ≤1.5mm |
Thickness of the cover layer >1.5mm |
||
|
The average value of the longitudinal specimen shall be no less than |
3 | 2.2 | 2.6 |
|
The peak value of the longitudinal specimen |
2 | 1.6 | 2.0 |
1. Specification
| Belt width (mm) | Sidewall height (mm) | Cleat height (mm) | Effective belt width (mm) |
| 400 | 60 | - | |
| 80 | 70 | ||
| 100 | 90 | ||
| 120 | 100 | ||
| 500 | 60 | 250 | |
| 80 | 70 | ||
| 100 | 90 | ||
| 120 | 110 | ||
| 160 | 140 | ||
| 650 | 60 | 250, 300, 350 | |
| 80 | 70 | ||
| 100 | 90 | ||
| 120 | 110 | ||
| 160 | 140 | ||
| 200 | 180 | ||
| 800 | 60 | 350, 410, 460 | |
| 80 | 70 | ||
| 100 | 90 | ||
| 120 | 110 | ||
| 160 | 140 | ||
| 200 | 180 | ||
| 240 | 220 | ||
| 1000 | 60 | 460, 550, 640, 690, | |
| 80 | 70 | ||
| 100 | 90 | ||
| 120 | 110 | ||
| 160 | 140 | ||
| 200 | 180 | ||
| 240 | 220 | ||
| 300 | 270 | ||
| 1200 | 60 | 460, 550, 640, 690 | |
| 80 | 70 | ||
| 100 | 90 | ||
| 120 | 110 | ||
| 160 | 140 | ||
| 200 | 180 | ||
| 240 | 220 | ||
| 300 | 270 |
Rubber conveyor belt
1.Ply:1-10plies
2.Width:120-2200mm
3.Thickness: 6-40mm
4. Cover Tensile Strength: 9-25MPA
Specifiction/strength:
160N/mm-----3150N/mm
Width:
100mm---2200mm
Ep80 Ep100 Ep125 Ep200 Ep250 Ep300 Ep400 Ep500 Ep600
NN80 NN100 NN125 NN200 NN250 NN300 NN400 NN500 NN600
Advantage:
1. Natural rubber Thin belt body with high strength, light weight.
2. Anti-abrasive, impact resistant, corrosion resistant
3. Softy belt body, good flexibility, excellent trough.
4. Vulcanization molding
5. Long service life
Features
1.Excellent elasticity
2.Anti-impact
3.High-adhesion
4.Good flexibility
5.Trough ability
6.Better stability of size
7.Resistance to water
Application
rubber conveyor belt is widely used in Harbour (port), Metallurgy, Mining, Electricity, Coal, Foundries, Construction, Food, Cement, Fertilizer, Copper, Pig Iron Ores, Sponge Iron Reserves etc.
rubber conveyor belt has over 10 key types according to the use classification:
conveyor belt are primarily used in the following industries:
| Standards | Cover Rubber | Adhesion | |||||
| Tensile Strength | Elongation at break | Abrasion | Cover to Ply | Cover to Ply | |||
| DIN 22102 | Mpa | % | mm3 | N/mm | N/mm | ||
| (<=1.5mm) | (>1.5mm) | ||||||
| DIN 22102-Z | 15 | 350 | 250 | 3.5 | 4.5 | ||
| DIN 22102-W | 18 | 400 | 90 | 3.5 | 4.5 | ||
| DIN 22102-Y | 20 | 400 | 150 | 3.5 | 4.5 | ||
| DIN 22102-X | 25 | 450 | 120 | 3.5 | 4.5 | ||
| Standards | Cover Rubber | Adhesion | |||||
| Tensile StrengTD | Elongation at break | Abrasion | Cover to Ply | Cover to Ply | Ply to Ply | ||
| AS 1332 | Mpa | % | mm3 | N/mm | N/mm | N/mm | |
| (<=1.9mm) | (>1.9mm) | ||||||
| AS 1332-N17 | 17 | 400 | 200 | 4 | 4.8 | 6 | |
| AS 1332-M24 | 24 | 450 | 125 | 4 | 4.8 | 6 | |
| Standards | Cover Rubber | Adhesion | |||||
| Tensile StrengTD | Elongation at break | Abrasion | Cover to Ply | Cover to Ply | Ply to Ply | ||
| RMA | Mpa | % | mm3 | N/mm | N/mm | N/mm | |
| (<=1.6mm) | (>1.6mm) | ||||||
| RMA-I | 17 | 400 | 3 | 4.4 | 4 | ||
| RMA-II | 14 | 400 | 3 | 4.4 | 4 | ||
| Standards | Cover Rubber | Adhesion | |||||
| Tensile StrengTD | Elongation at break | Abrasion | Cover to Ply | Cover to Ply | Ply to Ply | ||
| SANS 1173 | Mpa | % | mm3 | N/mm | N/mm | ||
| A | 18 | 400 | 70 | 5 | 7 | ||
| C | 20 | 400 | 150 | 5 | 7 | ||
| M | 25 | 450 | 120 | 5 | 7 | ||
| N | 17 | 400 | 150 | 5 | 7 | ||
Application
){kind=link}