| Customization: | Available |
|---|---|
| Type: | Conveyor Belt |
| Feature: | Wear-resistant, Heat-resistant, Tear-resistant, Flame-resistant, Cold-resistant |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Heat Resistant Rubber Conveyor Belt
Usage
Heat resistant conveyor belts are widely used in industries such as steel mills, cement plants, and foundries where materials are transported at high temperatures. These belts are designed to withstand heat and thermal stress, making them ideal for conveying hot materials such as clinker, slag, and hot powders.
|
The physical and mechanical properties of the heat resistant covering layer after tested should be in accordance with the following table: |
|||||
| Project | The type | ||||
| T1 | T2 | T3 | T4 | ||
| Change the range | |||||
| Hardness | Draw the intensity | 20 | 20 | 20 | 20 |
| Maximum after wearing out | 85 | ||||
| Draw the intensity |
The minimum value Mpa after wearing out |
12 | 10 | 5 | 5 |
| Performance rate of change /% | -25 | -30 | -40 | -40 | |
| Break person who extend | Performance rate of change /% | -50 | -50 | -55 | -55 |
| After aging rate of change /% | 200 | 200 | 180 | 180 | |
The heat resistance conveyor belt physical property of the cover rubber after heat test shall conform to the values specified in the table.
| Item | type | ||||||
| type I | type II | type III | |||||
| variable range | |||||||
| Hardness | Difference before and after ageing (IRHD) | ±20 | |||||
| Max. Value after ageing (IRHD) | 85 | ||||||
| Tensile strength | variable rate in performance <= | 25 | 30 | 40 | |||
| Min. value after ageing Mpa | 12 | 10 | 5 | ||||
| Rate of elongation at break | variable rate in performance% <= | 50 | 55 | ||||
| Min. value after ageing | 200 | 180 | |||||
The heat resistance conveyor belt abrasive wear of the cover rubber
| Type Item level | Abrasive wear | ||
| type I | type II | type III | |
| First quality | 0.8 | 1 | 1 |
| accepts | 1 | 1.2 | 1.2 |
The heat resistance conveyor belt layer to layer adhesion strength
| Item |
interlayer of cloth |
cover layer and cloth interlayer | |
|
Thickness of the cover layer ≤1.5mm |
Thickness of the cover layer >1.5mm |
||
|
The average value of the longitudinal specimen shall be no less than |
3 | 2.2 | 2.6 |
|
The peak value of the longitudinal specimen |
2 | 1.6 | 2.0 |
Production Environment
Rubber conveyor belt
Advantage:
Heat resistant conveyor belts are widely used in industries such as steel mills, cement plants, and foundries where materials are transported at high temperatures. These belts are designed to withstand heat and thermal stress, making them ideal for conveying hot materials such as clinker, slag, and hot powders.